No.
PURE
Type
Functional Groups
Ionic Form
Moisture
%
Volume Capacity mmol/ml
Shipping Weight
Approx. g/ml
True Density g/ml
Particle Size
%
Comments
Equivalents
(ROHM&HAAS)
Equivalents
(PUROLITE)
01
PC001
Strong Acid Poly-styrene
-SO3-
Na+
56-63
¡Ý 1.6
0.73-0.84
1.18-1.25
0.315-1.25mm ¡Ý 95
Gel type ; Resin designed for softening,especially small scale domestic.
IR118
C120E
02
Strong Acid Poly-styrene
-SO3-
Na+
45-50
¡Ý 1.9
0.77-0.87
1.25-1.28
0.315-1.25mm ¡Ý 95
Gel type ;the resin is the most widely used cation in water conditioning, inclduing water softening;deionization; split-stream dealkazation; separation of rare earths;separation of amino acids, wine stablization; etc.
IR120
C100E
03
Strong Acid Poly-styrene
-SO3-
Na+
43-48
¡Ý 2.0
0.78-0.88
1.25-1.30
0.315-1.25mm ¡Ý 95
Gel type ; Resin with high capacity for softening and demineralisation.
IR120
C100
04
Strong Acid Poly-styrene
-SO3-
Na+
40-46
¡Ý 2.0
0.80-0.88
1.25-1.34
0.315-1.25mm ¡Ý 95
Gel type with excellent resistance to oxidation.Gives particularly good separation from anion resin in mixed beds.
IR 122
C100X10
05
PC005
Strong Acid Poly-styrene
-SO3-
Na+
38-45
¡Ý 2.1
0.80-0.88
1.25-1.34
0.315-1.25mm ¡Ý 95
Gel type with excellent resistance to oxidation. High capacity.
-
C100X12
06
Strong Acid Poly-styrene
-SO3-
Na+
45-55
¡Ý 1.75
0.76-0.83
1.25-1.28
0.315-1.25mm ¡Ý 95
Macroporous type with excellent resistance to attrition and osmotic shock. For treatment of condensates,continuous processes and special applications(galvanic plating, sugar)
IR252
C150
¡¡
01
Poly-acrylic
COO -
H+
45-52
¡Ý 4.2
0.72-0.80
1.14-1.20
0.315-1.25mm ¡Ý95
Macroporous type. High Capacity. Removal of temporary hardness and alkalinity,waste water treatment, recovery of noble metals.
IRC 74/86
C104
02
PC210
Poly-acrylic
COO -
H+
45-55
¡Ý 3.5
0.70-0.78
1.12-1.20
0.315-1.25mm ¡Ý95
Very weakly acidic type for special applications (pharmaceutical, fixation of antibiotics)
IRC50
C115
¡¡
01
Poly-styrene Type I
-N+(CH3)3
Cl-
48-58
¡Ý 1.3
0.66-0.71
1.06-1.10
0.315-1.25mm ¡Ý95
Gel type; High operating capacity. Good silica removal.Good kinetics giving demineralisation to high purity.
IRA 402
A400
02
Poly-styrene Type I
-N+(CH3)3
Cl-
42-48
¡Ý 1.5
0.67-0.73
1.07-1.10
0.315-1.25mm ¡Ý95
Gel type; Good mechanical strength. Good silica removal.Make ultrapure water.
IRA400
A600
03
Poly-styrene Type II
Cl-
45-51
¡Ý 1.3
0.68-0.76
1.09-1.15
0.315-1.25mm ¡Ý95
Gel type ; Good kinetic and operating capacity. Good mechanical strength. For demineralisation,giving good silica removal in counter-flow regeneration.
IRA410
A300
04
Poly-styrene Type II
Cl-
37-44
¡Ý 1.4
0.68-0.76
1.09-1.15
0.315-1.25mm ¡Ý95
Gel type ; High capacity for demineralisation of water, especially for water source with higher salt content, separation of biochemicals.
-
A200
05
Poly-styrene Type I
-N+(CH3)3
Cl-
50-60
¡Ý 1.15
0.66-0.73
1.06-1.10
0.315-1.25mm ¡Ý95
Macroporous type ; Good mechanical and osmotic resistance. For condensate treatment and continuous systems. Good silica removal.
IRA900
A500
06
Poly-styrene Type II
Cl-
47-57
¡Ý 1.2
0.68-0.73
1.07-1.12
0.315-1.25mm ¡Ý95
Macroporous type ; High operationg capacity. Especially for water source with higher salt content,decolorization of sugar liquor and separation of biochemicals.
IRA910
A510
07
Poly-acrylic
-N+(R3)
Cl-
55-65
¡Ý 1.2
0.68-0.75
1.05-1.10
0.315-1.25mm ¡Ý95
Gel type. Good mechanical resistance. Reversibly removes organic with good resistance to fouling. For demineralisation of water and sugar decolorisation.
IRA458
A850
08
PA510
Poly-acrylic
-N+(R3)
Cl-
65-75
¡Ý 0.8
0.65-0.72
1.03-1.09
0.315-1.25mm ¡Ý95
Macroporous type ; Adsorbent resin for decolorisation of organic solution. Organic scavenger.
IRA958
A860
¡¡
01
Poly-styrene
-N(CH3)2.H2O
Free Base
50-60
¡Ý 1.4
0.65-0.72
1.04-1.07
0.315-1.25mm ¡Ý95
Macroporous type.resin optimised for demineralisation of water and saccharose, especially for water source with higher salt content.
IRA 93
A100
02
PA301
Poly-styrene
-N(CH3)2.H2O
Free Base
47-55
¡Ý 1.6
0.65-0.72
1.04-1.07
0.315-1.25mm ¡Ý95
Macroporous type.High capacityd for demineralisation/decolorisation of glucose and other organic solution.
IRA92
A103
03
Poly-acrylic
-N(CH3)2.H2O
Free Base
56-62
¡Ý 1.6
0.64-0.71
1.05-1.10
0.315-1.25mm ¡Ý95
Gel type. Demineralisaion of water high in organic matter, and organic solution(sugar juices). High operational capacity.
IRA 68/67
A845
04
PA511
Poly-acrylic
-N(CH3)2.H2O
Free Base
45-55
¡Ý 2.7
0.65-0.72
1.05-1.10
0.315-1.25mm ¡Ý95
Macroporous resin .Resistant to high organic.Special applications
IRA 60
A830
 
01
Mixed of PC003/PA101
-
H+/OH- 99%H+,90%OH-
-
-
0.70-0.78
-
0.315-1.25mm ¡Ý95
Ready for use regenerable mixed bed for water deionization with high silica removal efficiency and refine water for electrical home appliances,
MB20
MB400
02
PMB102
Mixed of PC003/PA102
-
H+/OH- 99%H+,90%OH-
-
-
0.70-0.78
-
0.315-1.25mm ¡Ý95
Ready for use regenerable mixed bed for ultrapure water system with high silica removal.
MB 9
MB46
03
PMB200
Mixed of PC002/PA200
-
H+/OH- 99%H+,90%OH-
-
-
0.68-0.76
-
0.315-1.25mm ¡Ý95
Ready for use regenerable mixed bed for water deionization with high silica removal efficiency and refine water for electrical home appliances
-
MB39
04
Mixed NRC001/NRA101
-
H+/OH- 99%H+,95%OH-
-
-
0.70-0.78
-
0.315-1.25mm ¡Ý95
Demineralization and decontamination of secondary cooling circuits/effluent. Excellent resistance to attrition
IRN150
NRW37LC
05
PMB224
Mixed NRC001/NRA102
-
H+/OH- 99%H+,95%OH-
-
-
0.70-0.78
-
0.315-1.25mm ¡Ý95
Ready for use regenerable mixed bed for ultrapure water system, very low TOC permeability & high attrition stability, refine water for eletrical home appliances.
-
NRW37SC
¡¡
01
Strong Acid Poly-styrene
-SO3-
99.9%/H+
45-50
¡Ý 1.8
0.74-0.83
1.25-1.28
0.4-1.25mm ¡Ý95
Removal of cations including radioactive isotopes from aqueous solutions
IRN77
NRW100
02
NRC100
Strong Acid Poly-styrene
-SO3-
99.9%/H+
45-55
¡Ý 1.7
0.73-0.82
1.18-1.25
0.4-1.25mm ¡Ý95
-
NRW150
03
Poly-styrene Type I
-N+(CH3)3
95%/OH-
53-60
¡Ý 1.0
0.66-0.71
1.06-1.10
0.4-1.25mm ¡Ý95
Removal of anions including radioactive isotopes from aqueous solutions
IRN78
NRW400
04
NRA102
Poly-styrene Type I
-N+(CH3)3
95%/OH-
42-48
¡Ý 1.1
0.66-0.73
1.07-1.10
0.4-1.25mm ¡Ý95
-
NRW600
05
NRA200
Poly-styrene Type I
-N+(CH3)3
95%/OH-
50-60
¡Ý 1.0
0.65-0.73
1.06-1.10
0.4-1.25mm ¡Ý95
-
NRW505
¡¡
01
Chelating
Amino-Diacetic
Na+
45-50
¡Ý 0.7
0.71-0.75
1.25-1.28
0.45-1.00mm ¡Ý95
Selective removal of polyvalent ions
IRC748
S930
02
Chelating
Amino-phosphonic
Na+
60-65
¡Ý 0.5
0.71-0.75
1.25-1.28
0.40-0.85mm ¡Ý95
Used for separation and recovery of heavy metals. Especially used for decalcification of brine.
IRC747
S940
03
PS420
Chelating
Thiouronium
H+
48-54
¡Ý 0.8
0.70-0.75
1.25-1.28
0.315-1.25mm ¡Ý95
Excellent selectivity and capacity for mercury removal.
GT73
S920
¡¡
01
PC002NS
Strong Acid
Sulphonic
Na+
45-50
¡Ý 1.8
0.77-0.87
1.25-1.28
0.315-1.25mm ¡Ý95
Gel type ; no-solvent , special food grade
-
-
02
PC003NS
Strong Acid
Sulphonic
Na+
43-48
¡Ý 1.9
0.79-0.86
1.25-1.28
0.315-1.25mm ¡Ý95
Gel type ; no-solvent , special food grade
-
-
03
PC101
Strong Acid
Sulphonic
H+
54-60
¡Ý 1.8
0.75-0.84
1.20-1.27
0.40-1.25mm ¡Ý95
As catalysts in synthetic industry( MTBE)
A35
CT175
04
PC200FD
Weak Acid
Carboxyl
H+
50-60
¡Ý 3.5
0.70-0.78
1.12-1.20
0.40-1.25mm = 96
used in potable water
-
C107E
05
PA202
Strong Base Anion
Quaternary Ammonium
Cl-
52-56
¡Ý 1.0
0.68-0.73
1.07-1.12
0.315-1.25mm ¡Ý95
Selectively removes nitrate in potable water.
IRA 996
A520
06
PA203
Strong Base Anion
Quaternary Ammonium
Cl-
40-50
¡Ý 0.75
0.68-0.73
1.07-1.12
0.40-0.71mm ¡Ý95
Selectively removes CLO3- in potable water.
-
A530
07
PB600
Adsorbent
No-funct.
-
50-60
-
0.65-0.72
1.05-1.10
0.40-0.71mm ¡Ý95
Adsorpition and separtion of non-polar substances in polar solution, decoloration and clearing of waste water in food and drinking industries
XAD 4
AP250
08
PI-TR
Inert Polymer
No-funct.
-
= 12
-
0.68-0.71
1.13-1.16
0.71-0.90mm ¡Ý95
Inert polymer beads for TRILITE system
359
IP-7

¡¡

PARTICLE SIZE-CATION RESIN ¡¡ PARTICLE SIZE-ATION RESIN
Pure Grade Size Range Limitation Application Pure Grade Size Range Limitation Application
STD 0.315-1.25mm ¡Ý 95% standard size STD 0.315-1.25mm ¡Ý 95% standard size
FC 0.45-1.25mm ¡Ý 95% Floating bed FC 0.45-1.25mm ¡Ý 95% Floating bed
SC(Strong) 0.63-1.25mm ¡Ý 95% Double compartment bed SC(Strong) 0.63-1.25mm ¡Ý 95% Double compartment bed
SC(Weak) 0.315-0.63mm ¡Ý 95% Double compartment bed SC(Weak) 0.315-0.63mm ¡Ý 95% Double compartment bed
TR 0.71-1.25mm ¡Ý 95% Tthree component mixed bed TR 0.45-0.90mm ¡Ý 95% Three component mixed bed
UN 0.40-0.71mm ¡Ý 95% Uniform Particle Size UN 0.40-0.71mm ¡Ý 95% Uniform Particle Size
¡¡
¡¡
Copyright(C)2005,Pure Resin Company Limited All Rights Reserved.
Supported by ChemNet ChinaChemNet Toocle